nichrome resistance wire

High-resistivity nickel-chromium alloys for use up to 1250º C (2280º F).

The high aluminum content, in combination with the high chromium content causes the scaling temperature to increase up to 1250°C (2282°F).

High-resistivity nickel-chromium alloys for use up to 1250º C (2280º F).

FeCrAl 0Cr27Al7Mo2:High temperature wire. Used in appliances where it has high resistivity and good oxidation resistance are of particular importance.

Higher hot and creep strength; Better ductility after use; Higher emissivity; Non-magnetic; Better wet corrosion resistance

High-resistivity nickel-chromium alloys for use up to 1250º C (2280º F).

FeCrAl 0Cr25Al5 is a high-temperature ferritic Alloy. Is used in electrical heating elements in industrial furnaces and in the appliance industry.

FeCrAl 0Cr23Al5 is widely used in industrial electric furnaces, household electrical appliances and far infrared ray devices. Has high resistance.

FeCrAl H23YU5(0Cr23Al5) is widely used in household electrical appliance,heating elements,mechanical manufacturing and other industrial fields.

FeCrAl 0Cr21Al6Nb is ferritic iron-chromium-aluminium alloy which is used at temperatures to 1350°C.Used in high-temperature furnaces in heat treating

FeCrAl 0Cr21Al4 alloy can replace Kanthal series. It is used for industrial furnaces, kilns & other equipment with highest operation temperatures.

It has characteristics of high resistance,low temperature coefficient of electric resistance, high operating temperature & good corrosion resistance.

H13YU4 (0Cr13Al4) posses the characteristics of high resistance, low temperature coefficient of electric resistance and good corrosion resistance.

FeCrAl (0Cr27Al7Mo2) Resistance Wire is made of iron chromium aluminum alloy. The scaling temperature is 1400°C (2552°F). Used in industrial furnace.

FeCrAl (0Cr21Al6Nb) Resistance Wire is made of iron chromium aluminum alloy. The scaling temperature is 1350°C (2462°F). Used in industrial furnace

low resistivity and high temperature coefficient of resistance. Good workability and high-temperature strength.

FeCrAl (0Cr21Al6) Resistance Wire is made of iron chromium aluminum bases containing small amounts of reactive elements such as yttrium and zirconium.

for generation, measurement and control of heat in all types of household appliances, such as small electric appliances, white goods and gas appliance

FeCrAl (0Cr25Al5) Resistance Wire is made of iron chromium aluminum alloy. The scaling temperature is 1250°C (2282°F). Max. operating temp. is 950°C.

FeCrAl 1Cr13Al4 Resistance Heating Wire is made of iron chromium aluminum alloy. The scaling temperature is 650°C (1202°F).Max. operating temp. 950°C.

1.High resistance, low temperature coefficient of electric resistance
2.Good corrosion resistance under high temperature
3.Diameter: 0.05mm-10.0mm

FeCrAl (0Cr21Al6Nb) Resistance Wire is made of iron chromium aluminum alloy. The scaling temperature is 1350°C (2462°F).

1.High resistance, low temperature coefficient
2.Good corrosion resistance under high temperature
3.Diameter: 0.05mm-10.00mm

1.High resistance, low temperature coefficient
2.Good corrosion resistance under high temperature
3.Diameter: 0.05mm-10.00mm

Higher maximum temperature in air; Longer life;Higher surface load;Better oxidation properties; Lower density;Higher resistivity;Higher yield strength

The Resistance Heating Elements program includes a wide range of wire used for wire mesh and filters.

max working temperature:1250°C. Double electro slag refining technique, rare earth element used. Outstanding thermal stability and working life.

1.High resistance, low temperature coefficient
2.Good corrosion resistance under high temperature
3.Diameter: 0.05mm-10.00mm

1.High resistance, low temperature coefficient
2.Good corrosion resistance under high temperature
3.Diameter: 0.05mm-10.00mm

1.High resistance, low temperature coefficient
2.Good corrosion resistance under high temperature
3.Diameter: 0.05mm-10.00mm