ptfe fiber packing

It is made of Dupont's Kevlar yarn impregnated with PTFE emulsion and processed with lubricant. As the strength and module of Kevlar is as high as the

Kevlar Rope packing is made of Du Pont's aramid yarn impregnated with PTFE dispersion and processed with lubricant. braided into square cross section.

Cotton PTFE fiber packing
Density (g/cm3):1.3

The packing is manufactured in the following procedures: polyacrylonitrile fibre is heated into carbonized fibre.

 
Electric insulation</sp

Temperature -100-+300
Pressure 35MPa
linear velocity 15m/s
Chemical Resistance PH value 2-12

 
PAN Fiber Braided

Double handle control system
Sinmens PLC control system

Kevlar fiber braided packing is made of DuPont's Kevlar yarn impregnated with PTFE dispersion and processed with lubricant, braided into square cross

Price:US$0.3;Productivity:6000KGS PER DAY;Min. Order:3 pcs;Packing:WOODEN CASE;Transportation:sea;DeliveryDate:5days;PaymentType:T/T;Trademark:QS;Spe

The cotton fiber packing is braided from cotton yarns which had been pre-impregnated. Intensively re-impregnated during braiding.

CARBON FIBER PACKING/Carbonized packing/Pan Fibre packing

It is a braided packing made of Aramid fiber. This packig can bear higher-pressure applications than other types of braided packings.

Braided from high quality Dupont Aramid/Kevlar fiber with PTFE Impregnation and lubricant additive. Extremely hard wearing.

Braided by aramid fiber and treated by lubricant and PTFE. It is used in acid, alkali, etc.
Pressure: 3Mpa in centrifugal pumps, 10 Mpa in piston p

Temperature -100-+300
Pressure 35MPa
linear velocity 15m/s
PH Value 2-12

Carbon Fiber Packing
The packing is woven of strong carbon fiber after softening treatment and impregnated with the mixture of fine graphite po

1. Packing made of synthetic fiber yarns
2. Packing needs impregnating with block agents, lubricants
3. Economic seal packing choice

Texturized fiberglass braided round packing, diameter: 3mm-50mm, roll length:10m-200m, weight: 25g/m-1950g/m, continuous temperature resistance:550℃

silica gel packing is made of silica core + glass fiber casing+ silicone coating,

Carbon Packing is made from carbonized fiber yarn treated with graphite particles, and then is braided to form packing.

Aramid fiber packing kevlar fiber packing nomex fiber packing are available from China FEITE Sealing Material Co Ltd

JX305 CARBON FIBER PACKING
The packing is woven of strong carbon fiber after softening treatment impregnation with the mixture of fine graphite

info(at)acsealing com Pure carbon fiber packing is Braided of caebon fiber? impregnated with proprietary lubricants and PTFE,? it has High pressure an

AT511L1 Comparing with the yellow aramid fiber packing, the Nomex Fiber Packing does not require high rigidity of the shafts.

High strength carbonized fiber packing is mede from imported carbonized fiber. And it is impregnated with PTFE latex, nami level graphite powder or ot

PTFE-graphite with kevlar fiber corner braided packing
Density (g/cm3):1.40-1.45

Braided from strong carbon continuous yarns after softening, impregnated with proprietary lubricants and graphite particles, which fill voids

Price:US$0.03;Productivity:6000kgs per day;Min. Order:3 kgs;Packing:wooden case;Transportation:sea;DeliveryDate:5days;PaymentType:T/T;Trademark:Qs;Sp

Less maintenance, easy to install, will not wear the pump shaft or the valve rod. The Ramie dipping PTFE can be required