Steel Material | 38CrMoALA,SKD61.,D2 etc. |
Hardness after Hardening&Termpering | HB240-280 |
Nitriding Treatment | ≥ 96 hours |
Surface Hardness | 58-64 HRC |
Nitrided layer depth | 0.5-0.8mm |
Surface Roughness | Ra0.4 |
Screw Straightness | 0.015mm |
Chromium-Plated Surface Hardness after nitriding | ≥900HB |
Chromium-Plating Layer Thickness | 0.05-0.10 mm |
Bimetallic Layer Hardness | 50-65 HRC |
Depth of Alloy Layer | 0.8-2.0 mm |