Heat ceramic fiber insulation board of 4 grades including standard, high pure, high
aluminium and zirconium adopt corresponding ceramic fiber bulk as raw material, vacuum
forming technology and dry process via drying machine guarantee our Ceramic Fiber
Board possesses delicate work. The 4 grades Ceramic Fiber Board also has close texture,
good tenacity, high intensity and anti wind-erosion nature except all the excellent
Heat ceramic fiber insulation board
Typical application:
aluminium and zirconium adopt corresponding ceramic fiber bulk as raw material, vacuum
forming technology and dry process via drying machine guarantee our Ceramic Fiber
Board possesses delicate work. The 4 grades Ceramic Fiber Board also has close texture,
good tenacity, high intensity and anti wind-erosion nature except all the excellent
Heat ceramic fiber insulation board
Typical application:
• Insulating backup to brick & castable
• Furnace hot face lining
• Use in industrial heat process equipment
• High temperature gasket & seals
• Flue & chimney linings in furnace & kilns
• Molten metal trough covers
• Expansion joint Industrial heat shields & thermal barriers
• Industrial combustion chamber construction
• Full thickness refractory lining
• High temperature boiler wall insulation
• Pouring forms for castable
Heat ceramic fiber insulation board
Heat ceramic fiber insulation board
Characteristic:
• Low thermal conductivity
• Low thermal capacity
• High thermal stability
• Resistance to thermal shock, flame and airflow attack
• High compressive strength and resistance to corrosion
• High toughness, easy to cut and install quickly
• Accurate thickness and size
• Shorter heat up and cool down time
Tech Data:
Standard | High Pure | High Aluminum | Zirconium | ||
Classifition temperature(oC) | 1260 | 1260 | 1360 | 1430 | |
Work temperature(oC) | 1050 | 1100 | 1200 | 1350 | |
Color | Pure white | Pure white | Pure white | Pure white | |
Density(kg/m3) | 280 | 280 | 280 | 280 | |
480 | 480 | 480 | 480 | ||
Permanent linear shrinkage(%) (after24hours,density320kg/m3) | -3 | -3 | -3 | -3 | |
(1000oC) | (1100oC) | (1200oC) | (1350oC) | ||
Thermal conductivity(w/m.k) density285kg/m3) | 0.085(400oC) | 0.085(400oC) | 0.085(400oC) | 0.085(400oC) | |
0.132(800oC) | 0.132(800oC) | 0.132(800oC) | 0.132(800oC) | ||
0.180(1000oC) | 0.180(1000oC) | 0.180(1000oC) | 0.180(1000oC) | ||
Compressive strength (Mpa) (thermal shrinkage 10%) | 0.5 | 0.5 | 0.5 | 0.5 | |
Chemical composition (%) | AL2O3 | 46 | 47-49 | 52-55 | 39-40 |
AL2O3+SIO2 | 97 | 99 | 99 | - | |
AL2O3+SIO2+Zro2 | - | - | - | 99 | |
Zro2 | - | - | - | 15-17 | |
Fe2O3 | <1.0 | 0.2 | 0.2 | 0.2 | |
Na2O+K2O | ≤0.5 | 0.2 | 0.2 | 0.2 | |
Size (mm) | 1200x1000; 1200x600; 1000X1000, 900x600; 600x300 | ||||
Thickness | 6-80mm | ||||