| 1, Specifications | |
| Material | 6063,6060,6061,6005 |
| Temper | T4,T5,T6 |
| Surface treatment | Mill Finish, Anodized, Powder, Coated, Wooden Finish, Polish |
| Color | Silver, Black, White, Red, Blue, and many colors can be available |
| Length | as required |
| Shape | Round, Square, Rectangular, Oval, Triangle, Hexagon, Octagon, or as per the drawings and samples |
| Fabrication | cutting, drilling, punching, milling, etc |
| Wall thickness | above 0.5mm |
| Outer diameter | from 8mm to 300mm |
| Package | inner plastic paper interleaving each piece profile, outer fixed by plywood, or as per your requirements |
| Delivery time | 10-12 days after order confirmation |
| Certification | ISO 9001:2008;ISO14001:2004;SGS |
| Warranty | 15 years |
| Application | industry, decoration, construction/ building, chairs, table, etc |
| Capacity | 3000 tons per month |
| 2, Standard Tubes Dimensions | |
| Round Tube Outer Diameter | 8mm,10mm,12mm,13mm,15mm,16mm,19mm,20mm.22mm,25mm,28mm,45mm,50mm, 60mm,70mm,100mm,etc |
| Square Tube Dimension | 8x8mm,12x12mm,20x20mm,25x25mm,50x50mm,etc |
| Rectangle Tube Dimension | 18x12mm,30x20mm,40x20mm,40x30mm,60x30mm,70x40mm,etc |
| 3, Primary Technical Data of Aluminum Tubes | ||||||||||
| 1) Chemical Composition | ||||||||||
| Alloy | Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti Impurity | Al | |
| 6063 | 0.2-0.6 | 0.35 | 0.1 | 0.1 | 0.45-0.9 | 0.1 | 0.1 | 0.1 | 0.15 | Rest |
| 6061 | 0.4-0.8 | 0.7 | 0.15-0.4 | 0.15 | 0.8-1.2 | 0.04-0.35 | 0.25 | 0.15 | 0.15 | Rest |
| 6060 | 0.3-0.6 | 0.1-0.3 | 0.1 | 0.1 | 0.35-0.6 | - | 0.15 | 0.1 | 0.15 | Rest |
| 6005 | 0.6-0.9 | 0.35 | 0.1 | 0.1 | 0.40-0.6 | 0.1 | 0.1 | 0.1 | 0.15 | Rest |
| 2) Mechanical Property | ||||
| Alloy | Temper | Tensile Strength | Yield Strength | Elongation |
| 6061 | T6 | ≥ 265Mpa | ≥ 245Mpa | ≥ 8% |
| 6063 | T5 | ≥ 160Mpa | ≥ 110Mpa | ≥ 8% |
| T6 | ≥ 205Mpa | ≥ 180Mpa | ≥ 8% | |
| 3) Anodized | |||
| Grade | Anodizing thickness | Hole scaling quality of oxide layer | |
| Average thickness | Local thickness | P. Cr acid-erosion weight less method | |
| AA10 | more than10um | more than8um | less than 30MG/d m 2 |
| AA15 | more than 15um | more than 12um | |
| 4) Powder coating & wooden-grained | ||
| Coating thickness | Coating impress rigidity | Adhesive force of coating layer |
| 40-120um | Indentation hardness >80 | O grade |