Features/Applications:
BH-2(LS) is manufactured with modified radiation cross-linked Polyolefin. The specially designed halogen free
formulation makes the tubing very flexible and shrinking at lower Temperature.Suitable for applications where heat
sensitive components protection e.g. PVC jacketed wire and cable and quick shrinkage is required. The flammability
of the tubing meets the automotive flame propagation standard MVSS 302 . although very flexible, BH-2(LS) has good
Mechanical and electrical performance.
Shrink ratio: 2:1
Operating temperature:-45 °C ~+125 °C
Minimum shrink temperature: 65 °C
Minimum fully recovery temperature: 95 °C
Meet: Sony SS-00259, RoHS
Standard color: Black
Technical Data:
Typical Data | ||
Tensile strength | ASTM D 2671 | 13MPa |
Elongation at break | ASTM D 2671 | 450% |
Tensile strength after aging at 158℃ for 168 hrs | ASTM D 2671 | 11MPa |
Elongation after aging at 158℃ for 168 hrs. | ASTM D 2671 | 300% |
Heat shock (250℃/ 4 hrs.) | ASTM D 2671 | No cracking |
Cold bend test (-55℃ / 4 hrs.) | ASTM D 2671 | No cracking |
Copper Corrosion | UL 224 | Pass |
Flammability | MVSS 302 | Pass |
Fluid resistance | 23℃ for 24hrs ISO 37 tensile strength Elongation | 11MPa 200% |
Longitudinal shrinkage | UL 224 | 0±5% |
Products Dimensions(mm/inch):
Normal size | As supplied (mm) | After recovered (mm) | Standard length (m/spool) | |
(inch) | Inside diameter (mm.) | Inside diameter (Max.) | Wall thickness (mm.) | |
1/16 | 1.6 | 0.8 | 0.50 | 200 |
3/64 | 2.4 | 1.2 | 0.50 | 200 |
1/8 | 3.2 | 1.6 | 0.50 | 200 |
3/16 | 4.8 | 2.4 | 0.50 | 200 |
1/4 | 6.4 | 3.2 | 0.60 | 100 |
5/16 | 8.0 | 4.0 | 0.60 | 100 |
3/8 | 9.5 | 4.8 | 0.60 | 100 |
1/2 | 12.7 | 6.4 | 0.60 | 50 |
5/8 | 16.0 | 8.0 | 0.60 | 50 |
3/4 | 19.1 | 9.5 | 0.80 | 50 |
1 | 25.4 | 12.7 | 0.90 | 50 |
1 1/4 | 31.8 | 15.9 | 0.90 | 50 |
1 1/2 | 38.1 | 19.1 | 1.00 | 50 |
2 | 50.8 | 25.4 | 1.10 | 50 |
Special size, cut pieces are available on request.