Wear Resistant Iron Ni Hard Liners Castings In Grey With HRc52~58 Hardness
Quick Details
1. Hardness:HRc52~58
2. International Standard:AS 2027-2002/Ni hard 4.
3. Specific weight or density:7.3~7.5g/mm2
Ni-hard Iron Castings Description:
1. Hardness: HRC52~58.
2. International Standard: AS 2027-2002/Ni hard 4.
3. Microstructure: Eutectic Carbide + Martensite + Residual Austenite
4. Specific weight or density: 7.3~7.5g/mm2
5. Break Point: 25~40kg/mm2.
In the recent 20 years, our liners have been widely used in large, medium and small ball mills in Chinese power generation, mining, cement, Chemical engineering and metallurgical industries and super fine pulverizing equipments. It is the only recommended liner product in the latest standard of the electric-power industry in China.
Technical Parameters
Wuxi Orient Anti-wear Engineering Co., Ltd.
Chemical Composition & Mechanical Property of Wear-resistant Castings
Item |
Cr-Mo Alloy Steel I |
Cr-Mo Alloy Steel II |
Cr-Mo Alloy Steel III |
High Cr white iron |
High Cr Alloy Steel |
High Manganese Steel |
Ni-Hard cast iron |
C |
0.30~0.50 |
0.65~0.90 |
0.40~0.90 |
2.40~3.20 |
1.1~2.2 |
0.90~1.30 |
2.40~3.60 |
Si |
0.50~1.20 |
≤0.75 |
0.70~1.20 |
0.60~1.20 |
0.60~1.20 |
≤0.08 |
≤0.80 |
Mn |
0.40~1.20 |
0.50~1.20 |
0.60~1.00 |
0.50~1.00 |
0.50~1.00 |
11.00~18.00 |
≤2.0 |
Cr |
1.70~2.50 |
1.50~2.50 |
4.00~7.00 |
12.00~30.00 |
11.00~30.00 |
1.50~2.50 |
1.5~10 |
S |
≤0.04 |
≤0.06 |
≤0.04 |
≤0.04 |
≤0.04 |
≤0.04 |
≤0.15 |
P |
≤0.04 |
≤0.06 |
≤0.06 |
≤0.06 |
≤0.06 |
≤0.06 |
≤0.15 |
Mo |
≤0.5 |
≤0.5 |
≤0.5 |
0.10~3.0 |
0.10~3.0 |
≤1.0 |
≤0.10 |
Cu |
0.10~0.60 |
≤0.25 |