lead dioxide coated titanium anode for Electrolytic Synthesis of Organic
Taijin Pbo2 coatedTi electrode is a new type of shift in the lead base metal anode, is a combination of precious metal coating and lead oxide anode. This novel anode is belong to lead anode derivative products, it take over the advantages of coated titanium anode and lead anode, also overcome the disadvantages of lead anode easy to bend or corrosion, as well as the high price in Ti coated anode.Perfectly in line with the trend and direction of anode of hydrometallurgyindustrydevelopment.
From the aspects of saving energy and reducing resource consumption and environmental protection,Pbo2 coatedTi electrodeis a kind of higher comprehensive properties novel anode.
Application |
1.Used as electrode anode materials, including electrolytic manufacturing of chromic acid, perchlorate, electrolytic oxidation method to purify the wastewater to reduce COD 2.Electrolytic smelting metals,Due to Pbo2 coatedTi electrode is resistanttosulfuric acids, suitable for electrodeposition insoluble anode materials in Zinc, Copper, Nickel, Cobalt sulfate, etc 3.Oil and water separation 4.Zinc plating, passivation, waste recycling; 5.Cathode anticorrosion 6.Neutral electrolytedephosphorization
|
Advantages |
1.Good electrical conductivity, high hydrogen evolutionoverpotentiality, good catalytic property,corrosion preventive, stable chemical properties, high electrochemically, allow passing a large current 2.Chemical stability,a lot of oxidant and acid have no effect on anode 3.good corrosion preventive and long life time(Especially shows long life in sulfuric acid solution andOrganic electrolyte). 4.hardness, abrasion resistance, low cost,. 5.Dimensionalstability, small space between the electrodes in using process,to solve the traditional lead anodefracture problems in solid, liquid and gas environment 6.Green,not to pollutebath solution,high quality 7.Ti base can reusable |
Product Features
Base metal | Gr1, Gr2, TA1 |
Current range | <5000A/m2 |
Temperature range | <80 ℃ |
Coating material | PbO2 |
Vitriol concentration | <30% |
Coating thickness | 0.2-0.5mm |
pH about the environment | 1-12 |
Shape | mesh, plates, tubes, rods, etc. |
1.High erosinon-resisting
2.High current efficiency
3.Long durability
4.Floor can circle after electrodes lose activity
5.No pollution to solution