310 310s Stainless Steel Wire Mesh,Stainless steel wire mesh
Stainless Steel 310 Mesh has good strength as well as excellent corrosion resistance at the high temperature up to 2100of or 1149oC.
Consisting of significant content of chromium and nickel, Stainless Steel 310 Mesh provides better performance in resisting general and localized corrosion than SS 304 mesh. It is a proven material for high temperature filtration elements.
Features of 310s stainless steel wire mesh
310S stainless steel(2520), due to high content of Ni and Cr, it is with good oxidation resistance, corrosion resistance, acid and alkali resistance, high temperature resistance. The maximum service temperature is 1200℃
310/310S Stainless Steel Wire Mesh Chemistry
| Element | Cr | Ni | C | Si | Mn | P | S | Mo | Cu | Fe |
| SS 310 | 24 – 26 % | 19.2 – 22 % | 0.25 % | 1.50 % | 2 % | 0.045 % | .03 % | 0.75 % | 0.50 % | Bal |
| SS 310S | 24 – 26 % | 19.2 – 22 % | 0.25 % | 1.50 % | 2 % | 0.045 % | .03 % | 0.75 % | 0.50 % | Bal |
Stainless Steel 310/310S Mesh Property Data
| Density (lb / cu. in.) | 0.289 |
| Specific Gravity | 7.9 |
| Specific Heat (Btu/lb/Deg F – [32-212 Deg F]) | 0.12 |
| Electrical Resistivity (microhm-cm (at 68 Deg F)) | 468 |
| Melting Point (Deg F) | 2650 |
| Modulus of Elasticity Tension | 30 |
| Mean coefficient of thermal expansion | 8.8 x 10(6)per oF, 15 x 10(6) per oC |
| Elastic modulus | 29 Psi x 10(6) or 200 GPa |
| Yield strength 0.2 percent offset | 45 ksi or 310 MPa |
| Tensile strength | 95 ksi or 655 MPa |
| Reduction of area % | 69 % |
| Hardness Rockwell B | 85 |