ER308LSI 309 316L 317L 347 410 welding wire

AWS

C

Si

Mn

Cr

Ni

Mo

S.P

Rm(MPa)

A5(%)

LA307

 E307T0-1

 E307T0-4

0.09

0.6

4.25

19.47

1.15

1.3

≤0.03

613

46

LA308L

E308LT1-1 

E308LT1-4

0.028

0.69

1.26

20.27

10.82

≤0.03

553

43

LA309L

E309LT0-1  

E309LT0-4

0.030

0.59

1.21

23.11

13.56

0.04

≤0.03

557

42

LA309Mo

E309LoMoT0-1

E309LoMot0-4

0.027

0.71

1.17

23.68

14.86

2.49

≤0.03

541

35

LA316L

E316LT0-1  

E316LT0-4

0.029

0.57

1.33

18.35

12.49

2.42

≤0.03

516

44

Brand

(mm)
Diameter

Shielding Gas

Chemical Composition of Deposited Metal(%)

C

Si

Mn

P

S

Cr

Ni

Mo

Cu

ER308

0.6-4.0

Ar+0.5

-2%CO2

0.08

0.3-0.65

1.0-2.5

0.03

0.03

19.5-22.0

9.0

-11.0

0.75

0.75

ER308L

0.6-4.0

Ar+0.5

-2%CO2

0.03

0.3-0.65

1.0-2.5

0.03

0.03

19.5-22.0

9.0

-11.0

0.75

0.75

ER308LSI

0.6-4.0

Ar+0.5

-2%CO2

0.03

0.65-1.0

1.0-2.5

0.03

0.03

19.5-22.0

9.0

-11.0

0.75

0.75

ER309

0.6-4.0

Ar+0.5

-2%CO2

0.12

0.3-0.65

1.0-2.5

0.03

0.03

23.0-25.0

12.0

-14.0

0.75

0.75

ER309L

0.6-4.0

Ar+0.5

-2%CO2

0.03

0.3-0.65

1.0-2.5

0.03

0.03

23.0-25.0

12.0

-14.0

0.75

0.75

ER310

0.6-4.0

Ar+0.5

-2%CO2

0.08-0.15

03-0.65

1.0-2.5

0.03

0.03

25.0-28.0

20.0

-22.5

0.75

0.75

ER312

0.6-4.0

Ar+0.5

-2%CO2

0.15

0.3-0.62

1.0-2.5

0.03

0.03

28.0-32.0

8.0

-10.5

0.75

0.75

ER316

0.6-4.0

Ar+0.5

-2%CO2

0.08

0.3-0.65

1.0-2.5

0.03

0.03

18.0-20.0

11.0

-14.0

2.0-3.0

0.75

ER316L

0.6-4.0

Ar+0.5

-2%CO2

0.03

0.3-0.65

1.0-2.5

0.03

0.03

18.0-20.0

11.0

-14.0

2.0-3.0

0.75

ER316LSI

0.6-4.0

Ar+0.5

-2%CO2

0.03

0.65-1.0

1.0-2.5

0.03

0.03

18.0-20.0

11.4

-14.0

2.0-3.0

0.75

ER410

0.6-4.0

Ar+0.5

-2%CO2

0.12

0.5

0.6

0.03

0.03

11.5-13.5

0.6

0.75

0.75

ER430

0.6-4.0

Ar+0.5

-2%CO2

0.1

0.5

0.6

0.03

0.03

15.5-17.0

0.6

0.75

0.75

≤0.08

0.30~0.65

1.00~2.50

19.00~22.00

9.0~11.0

≤0.03

≤0.03

≤0.75

≤0.75

MPa

%

570~610

36~42