ZG-P-8755/ZG-I-7118,High Density Upper Sole PU Resin,White Sole PU Resin
High Density Upper Sole PU Resin
White Sole PU Resin
Q/ZHTY 01—2013
Application: Low hardness, high density.
Characteristic: Suitable for shoes production.
Typical properties of pu resin
Name of products | Appearance | Viscosity(Pa·s/50℃) | Density(g/cm3/40℃) | Packge(kg) |
ZG-P-8755 | White or pale yellow,liquid foreign material | 0.75-0.95 | 1.16-1.20 | 18 |
ZG-I-7118 | Tranparent and pure liquid | 0.20-0.40 | 1.18-1.20 | 20 |
Reference shipments ratio: A/B=30 / 25(barrel)
Catalysts and auxiliary agents:
ZG-P-8755/ZG-AC-2/water/hardener=18kg/230g/70~90g/300-500g
Endurance High Density Sole PU Resin
Note: corresponding adjustment should be made to the addition of auxiliary agent at different areas, different environment and different production conditions.
Typical processing parameters& Typcal properties:
Reaction characteristics | technical standards | Test item | Physical properties |
Reference ratioP+C/I | 100/88-92 | Molded density(g/cm3) | 0.42-0.50 |
Material temperature(℃) | A material: 40-45; B material: 38-42 | Hardness(type C) | 70~80 |
Cream time(s) | 5~8 | Tensile strength(kgf/cm) | >10 |
End of Rise time(s) | 25~35 | Elingation(％) | 350~500 |
Metal mold temperature(℃) | 45~55 | DIN | <200 |
Demould time(min) | 3.0~6.0 | Free rise foam density(g/cm3) | 0.28-0.34 |
Folding resistance at room temperature | >100000 times | Folding(room temperature)(40,000 gap length mm) | ＜8 |
Sole PU Resin For Shoes Production
With the best ratio is based on the ratio, the ratio of value added with The type and quantity of paint additives vary.
The free foam density according to the seasons (temperature, humidity) vary
Ejection time with the increase of the thickness of molded extension
Folding conditions: angle of 90 degrees of flex, frequency of 80 times / min * 4 million
Data listed above are just for reference. The detail data are subjected to practical operation. If other requests for physical properties, please contact us.