Hastelloy B Wire is capable of withstanding high temperature, stress, severe corrosion and erosion prone environment, Hastelloy B Wire were found extensively usage in nuclear and chemical reactors, pipes and valves in diverse chemical industries. The predominant ingredient used in our Hastlealloy B Wire is high grade metal Nickel. The other grades that we offer our clients are Hastelloy C Wire and Hastelloy X Wire. follows are main introductions of Hastelloy X Wire.
Hastelloy B Wire Characteristic:
·Control of iron and chromium content to a minimum to prevent the generation of β-phase Ni4Mo.
·Excellent corrosion resistance of restore environment.
·An excellent resist to concentration sulfuric acid medium and large number of non-oxidizing acid corrosion.
·A very good resistance of chloride reduction of stress corrosion cracking (SCC).
·Good corrosion resistance of various organic acids.
Metallurgical structure:
Hastelloy B Wire is the face-centered cubic lattice structure. By controlling the content of iron and chromium at the minimum to reduce the processing brittle, prevent Ni4Mo precipitation during 1330-1380 ℃.
Hastelloy B Wire is the face-centered cubic lattice structure. By controlling the content of iron and chromium at the minimum to reduce the processing brittle, prevent Ni4Mo precipitation during 1330-1380 ℃.
Corrosion resistance:
Ni-Mo alloy Hastelloy B Wire, the carbon and silicon content is extremely low, reducing the HAZ carbon and other impurities precipitation, so the weld has sufficient corrosion resistance. Alloy Hastelloy B Wire in the reduction of medium with very good corrosion resistance, such as a various temperature and concentration of hydrochloric acid. In the middle of the concentration of sulfuric acid solution (or contain a certain amount of chloride ions) also has very good corrosion resistance. At the same time can be used to acetic acid and phosphoric acid environment. Alloy material suitable only in the metallurgical structure and pure crystal structure in order to have the best corrosion resistance.
Ni-Mo alloy Hastelloy B Wire, the carbon and silicon content is extremely low, reducing the HAZ carbon and other impurities precipitation, so the weld has sufficient corrosion resistance. Alloy Hastelloy B Wire in the reduction of medium with very good corrosion resistance, such as a various temperature and concentration of hydrochloric acid. In the middle of the concentration of sulfuric acid solution (or contain a certain amount of chloride ions) also has very good corrosion resistance. At the same time can be used to acetic acid and phosphoric acid environment. Alloy material suitable only in the metallurgical structure and pure crystal structure in order to have the best corrosion resistance.
Hastelloy B Wire Applied field:
Alloy Hastelloy B Wire with a wide range of applications in the field of chemical, petrochemical, energy manufacturing and pollution control , particularly in the sulfuric acid, hydrochloric acid, phosphoric acid, acetic acid, and other industries.
Alloy Hastelloy B Wire with a wide range of applications in the field of chemical, petrochemical, energy manufacturing and pollution control , particularly in the sulfuric acid, hydrochloric acid, phosphoric acid, acetic acid, and other industries.
Hastelloy B Wire Chemical compostion:
Aolly | C | Mn | Si | P | S | Cr | Ni | Mo | Fe |
Hastelloy B Wire | ≤0.05 | ≤1.00 | ≤1.00 | ≤0.030 | ≤0.030 | ≤1.00 | 58.0 ~64.0 | 26.0 ~30.0 | 4.0 ~6.0 |
Hastelloy B Wire Physical properties:
Density | 9.24g/cm3 |
Melting point | 1330-1380℃ |
Hastelloy B Wire Alloy minimum mechanical properties in the room temperature:
Alloy state | Tensile strength Rm N/mm2 | Yield strength RP0.2N/mm2 | Elongation A5 % |
Hastelloy B Wire | 690 | 310 | 40 |
Wire Further Processing | Cut to length Wire |
Flat Wire | |
Square and Shaped Wire | |
Rewinding and spooling | |
Polishing and cleaning |
Customer Service has more information about Wire Further Processing.