Basic Info.
  • Stainless Steel Wire: 301 Stainless Steel 
  • Place of Origin: Hebei  
  • Min.Order: 100 Kilogram
  • Means of Transport: Ocean, Air, Land
Supply Capacity
  • Production Capacity: 2000 Ton/Month
  • Packing:Reeled and Sealed Up
  • Delivery Date: 3-30days
301Stainless Steel Wire
301 stainless steel wire is a commonly available austenitic stainless with good corrosion resistance and elevated carbon to allow for cold working to a variety of tempers. It can be obtained in the annealed, 1/4 hard, 1/2 hard, 3/4 hard, full hard.

Wire Diameter
: 0.05mm-10.0mm, 0.002 Inch to 0.3937 Inch

301Stainless Steel Wire Chemistry Data:
Carbon
0.15 max
Chromium
16 - 18
Iron
Balance
Manganese
2 max
Nickel
6 - 8
Phosphorus
0.045 max
Silicon
1 max
Sulphur
0.03 max

301Stainless Steel Wire Physical Data:
Density (lb / cu. in.)
0.29
Specific Gravity
7.8
Specific Heat (Btu/lb/Deg F - [32-212 Deg F])
0.12
Electrical Resistivity (microhm-cm (at 68 Deg F))
432
Modulus of Elasticity Tension
28

Mechanical Properties
Grade 301 Temper ASTM A666
Tensile Strength (MPa) min.
Yield Strength 0.2% Proof (MPa) min.
Elongation (% in 50mm) (thick.>0.76mm) min.
Bend Test (thickness > 1.27mm)
Bend Angle (°)
Factor
Annealed
515
205
40
-
-
1/16 Hard
620
310
40
180
1
1/8 Hard
690
380
40
180
1
1/4 Hard
860
515
25
90
2
1/2 Hard
1035
760
18
90
2
3/4 Hard
1205
930
12
90
3
Full Hard
1275
965
9
90
5

Applications
Automotive trim, kitchen equipment, hose clamps, wheel covers, aircraft components and a wide variety of industrial applications.

Welding
All popular techniques may be used, however the material will lose temper in the heat affected weld zone.

Forging
Commence forging at 2000-2200 F(1093-1204 C) and finish at 1700 F(927 C).

Hot Working
While cold forming is recommended wherever feasible, forging, upsetting and other operations can be performed at 1800-2100 F. Temperatures above this range will cause scaling and a reduction in the workability of the material. Post-process annealing is required to re-attain maximum corrosion resistant properties.

Cold Working
Most common cold work methods are successful with this alloy. It should be understood however that the material will be more difficult to work than other austenitic stainless steels due its high work hardening rate. The resulting hardening will, however, produce increases in strength and toughness which may be of value in the finished product.

Annealing
1850-2050 F (101-1121 C) followed by rapid cooling. For thin sections air cooling is acceptable, while heavier sections should be water quenched.

Hardening
This alloy does not respond to heat treatment.

Wire Further Processing
Cut to length Wire
Flat Wire
Square and Shaped Wire
Rewinding and spooling
Polishing and cleaning



Send message to this supplier
Mr. Jialiang Zhao (Manager)
Tel: 86-10-64733806
Mobile: 86-13426315876
Enter between 20 to 3,000 chatacters.
Contact Method
Heanjia Super-metals Co., Ltd.
Room 2108, 21/F, BLK 128, Yinling International Zone,Wangjing West Road, Chaoyang District,, Beijing, China (Mainland) / 053600
Fax: 86-10-64733806
Didn't find what you're looking for? Post Buying Lead or contact our customer service specialist for help!
Buyer Help Center