Specifications & Sizes:
Stainless steel shot (0.2~2.5mm)
Shape: Conditioned
Sizes & specifications: In accordance with SAEJ441, AMS 2431 standards
Stainless steel shot (0.2~2.5mm)
Shape: Conditioned
Sizes & specifications: In accordance with SAEJ441, AMS 2431 standards
Chemical Composition:
304 Austenite: C<0.25%, Cr=16~18%, Ni=6~10%, Si<1%, Mn<2%
430 Austenite: C<0.25%, Cr=16~18%, Si<1%, Mn<1%
410 Austenite: C<0.25%, Cr=11~13%, Si<1%, Mn<1%
Note: Required products with other chemical components by clients can also be provided.
304 Austenite: C<0.25%, Cr=16~18%, Ni=6~10%, Si<1%, Mn<2%
430 Austenite: C<0.25%, Cr=16~18%, Si<1%, Mn<1%
410 Austenite: C<0.25%, Cr=11~13%, Si<1%, Mn<1%
Note: Required products with other chemical components by clients can also be provided.
Microhardness: 308~509 HV Vickers 32~50HRC Rockwell
Tensile intension: 490~1520 Mpa
Durablity: 6500 Times(1.0mm, VDF18001)
Microstructure: 304Type: Deformed Austenite
430Type: Deformed Ferrite
410Type: Deformed Martensite
Density: 7.8g/cm3
Bulk density: 4.7 g/cm3
Note: Part of the 304 Austenite stainless steel shot will convert into Martensite type, getting magnetic through a process of drawing, cutting and rounding
Tensile intension: 490~1520 Mpa
Durablity: 6500 Times(1.0mm, VDF18001)
Microstructure: 304Type: Deformed Austenite
430Type: Deformed Ferrite
410Type: Deformed Martensite
Density: 7.8g/cm3
Bulk density: 4.7 g/cm3
Note: Part of the 304 Austenite stainless steel shot will convert into Martensite type, getting magnetic through a process of drawing, cutting and rounding