Film faced phenolic poplarPlywood features a surface paper film impregnated with a phenolic resin and applied under heat and pressure. It was originally used primarily for fine faced concrete work and vehicle building. Phenolic plywood is also now used in access towers and scaffolding systems.
The plywood is edge sealed to minimise the ingress of water.
Film faced plywood is available with a smooth glass like finish on both faces or with a mesh pattern imprinted on the face to improve anti slip properties.
The surfaces are hard wearing, and different weights of film are available to suit the abrasion and wearing performance required.
| Product | Film Faced Plywood |
| Standard Size | 2440x1220mm OR 915x2135mm |
| Thickness | 9mm~25mm |
| Species Core | Poplar, Combi, Hardwood |
| Film | Dynea Film, Brown Film, Red film, Black film |
| Grade | A/A |
| Glue | Phenolic WBP, Melamine WBP, MR |
| Moisture | Below 12% |
TECHNICAL SPECIFICATION | ||||||
PRODUCT: | FILM FACED PLYWOOD | SPECIES: | COMBI | |||
SIZE: | 18MMX1220X2440 | GLUE: | MELAMINE WBP | |||
FILM: | BROWN | GRAMMAGE: | 120G/M2 | |||
Sr.No. | PROPERTY | UNIT | TEST METHOD | VALUE OF TEST | RESULT | |
1 | MOISTURE CONTENT | % | EN322 | 8% | Check Out | |
2 | DENSITY | KG/CBM | EN323 | 570 | Check Out | |
3 | BONDING QUALITY | BONDING QUALITY | MPA | EN314 | MAX:1.67 | Check Out |
MIN:0.85 | ||||||
DAMAGE RATE | % | ---- | 64% | |||
4 | BENDING MODULES OF ELASTICTY | LONGGITUDINAL | MPA | EN310 | 6800 | Check Out |
LATERAL | 5920 | |||||
5 | BENDING STRENGTH N/MM | LONGGITUDINAL | MPA | 63.6 | ||
LATERAL | 46.3 | |||||
6 | CYCLE LIFE | ABOUT 8~15 PEPEATED USING TIMES ACCORDING PROJECTES BY FORMWORK APPLICATION | ||||