EVA (Ethylene Vinyl Acetate copolymer)
Specifications
Product specifications | H_10 | H-17 | H-18 | H-56 | H-70 |
Solid Cotent% | 56±2 | 56±2 | 56±2 | 60±2 | 50±2 |
Cotent of Ethylene | 16±2 | 23±2 | 26±2 | 12±2 | 35±2 |
Viscositympa.s) | 3000±750 | 2500±500 | 3500±750 | 3000±750 | ≤1000 |
PH value | 5.0±1 | 5.0±1 | 5.0±1 | 5.0±1 | 5.0±1 |
Glass Transition (Tg)/ | 8±3 | 10±3 | 0±3 | 11±3 | 18±3 |
particle size(um) | 0.8 | 0.9 | 0.8 | 0.8 | 0.9 |
ResiduesWt%) | ≤0.3 | ≤0.3 | ≤0.3 | ≤0.3 | ≤0.3 |
Minium film-forming temperature | 0 | 0 | 0 | 0 | 0 |
valid period(days) | 180 | 180 | 180 | 150 | 150 |
Test Items | Unit | Typical Value | ||
MG80018 | MG80018-105 | MG80018-125 | ||
Density(23°C) | g/cm3 | 1.4 | 1.41 | 1.39 |
Tensile strength | MPa | 13.5 | 13.7 | 14.1 |
Elongation at break | % | 220 | 210 | 230 |
Hot setting test | 200°C x 15min, 0.2MPa | |||
Elongation under load | % | - | 90 | 75 |
Oven aging test | °C×h | 100×136 | 136×168 | 158×168 |
Permanent elongation after cooling | % | - | 5 | 6 |
Retention of Tensile strength | % | 110 | 109 | 112 |
Retention of Elongation at break | % | 86 | 88 | 87 |
low temperature brittleness | °C | -25 | -25 | -25 |
20°C Volume resistivity | Ω·cm | 3.6x1013 | 2.6x1013 | 4.1x1013 |
Dielectric strength | MV/m | 28 | 27 | 27 |
Oxygen index | % | 31 | 32 | 31 |
Application:
1.it's used in pigment,paint,coating
2.CAS No.:24937-78-8
3.Main Raw Material: Acry
2.CAS No.:24937-78-8
3.Main Raw Material: Acry
Package:25kg/PP bag,20MT/20FCL