Material: carbon steel, alloy steel, stainless steel
Forging type: open-die forging, hot forging
Forging weight: 1340kg
Billets weight: 1435kg
Maximum diameter: 1037mm
Initial forging temperature: 1200°C
Final forging temperature: 800°C
Post-forge cooling: furnace cooling
Heat treatment after forging: normalizing + tempering
Forged process: hot-forged, N or Q+T., then rough machining perform UT test
Standards: ASTM, ASME, DIN, SIS and EURONORM
QA DOC: chemical composition report, mechanical properties report, UT report, heat treatment report, dimensions check report
Inspection: the third party
Packing: wooden cases, wooden pallets
Material: carbon steel, alloy steel, stainless steel
Forging type: open-die forging, hot forging
Forging weight: 1340kg
Billets weight: 1435kg
Maximum diameter: 1037mm
Initial forging temperature: 1200°C
Final forging temperature: 800°C
Post-forge cooling: furnace cooling
Heat treatment after forging: normalizing + tempering
Forged process: hot-forged, N or Q+T., then rough machining perform UT test
Standards: ASTM, ASME, DIN, SIS and EURONORM
QA DOC: chemical composition report, mechanical properties report, UT report, heat treatment report, dimensions check report
Inspection: the third party
Packing: wooden cases, wooden pallets
Material: carbon steel, alloy steel, stainless steel
Forging type: open-die forging, hot forging
Forging weight: 1340kg
Billets weight: 1435kg
Maximum diameter: 1037mm
Initial forging temperature: 1200°C
Final forging temperature: 800°C
Post-forge cooling: furnace cooling
Heat treatment after forging: normalizing + tempering
Forged process: hot-forged, N or Q+T., then rough machining perform UT test
Standards: ASTM, ASME, DIN, SIS and EURONORM
QA DOC: chemical composition report, mechanical properties report, UT report, heat treatment report, dimensions check report
Inspection: the third party
Packing: wooden cases, wooden pallets