1. Material: 100% Nitrile Latex (Synthetic Rubber).
2. Particle Count: Max. 2000 /cm2 (Tested in accordance to IES-RP-CC-005.2)
3. Trace Elements: Trace elements (symbol) Maximum
Fluoride (F) 0.5 mg/cm2
Chloride (Cl) 2.0 mg/cm2
Bromide (Br) 0.5 mg/cm2
Nitrate (NO3) 1.0 mg/cm2
Phosphate (PO4) 0.5 mg/cm2
Sulfate (SO4) 0.5 mg/cm2
Sodium (Na) 0.5 mg/cm2
Potassium (K) 0.5 mg/cm2
(Tested in accordance to IES-RP-CC-005.2)
4. Copper Strip Test: No Discoloration.
5. FTIR: Silicone oil, Amide, DOP not detectable. (Tested in accordance to IES-RP-CC-005.2)
6. Non-volatile residue: Max. 30 mg/g. (Tested in accordance to IES-RP-CC-005.2)
7. Surface Resistivity: Max. 10e11 ohms/square. (Tested in accordance to ASTM-D257)
8. Static Decay: Max. 3 seconds. (Tested in accordance to FTMS 101-C, 4046)
9. Triboelectric charge: Max. 50 volts.
10. Color: White.
11. Design and Feature: Ambidextrous, straight fingers, textured or smooth and beaded cuff.
12. Dimensions: Glove size Palm width (mm) Length (mm)
Extra-small 70 ±10 min. 240mm
Small 80 ±10 min. 240mm
Medium 95 ±10 min. 240mm
Large 110 ±10 min. 240mm
Extra-large 115 ±10 min. 240mm
13. Thickness: Location of thickness measurements
Finger (at 15mm from fingertip) min. 0.28mm
Palm (at center of palm) min. 0.20mm
14. Physical Properties: Before aging After aging
Tensile Strength (Mpa): Min. 18 (Before Aging) min. 16 (After Aging)
Ultimate Elongation (%): Min. 500 (Before Aging) min. 400 (After Aging)
15. Packaging: 100 pieces of gloves per double polybags, 10 polybags per master polybag, 1 master polybag per carton.
Note: Inner & outer polybags are manufactured & processed in Class 100 Cleanroom
16. Certificate of: A certificate of conformance is available upon request to ensure all products shipped conform to specified specification.
17. Quality Assurance: Manufactured under ISO 9002 Quality System.
Meet or exceed ASTM D3578-95 on water leak & dimension.
The information above is a guideline of typical performance values and characteristics of the products & not to be use as actual product specifications.
2. Particle Count: Max. 2000 /cm2 (Tested in accordance to IES-RP-CC-005.2)
3. Trace Elements: Trace elements (symbol) Maximum
Fluoride (F) 0.5 mg/cm2
Chloride (Cl) 2.0 mg/cm2
Bromide (Br) 0.5 mg/cm2
Nitrate (NO3) 1.0 mg/cm2
Phosphate (PO4) 0.5 mg/cm2
Sulfate (SO4) 0.5 mg/cm2
Sodium (Na) 0.5 mg/cm2
Potassium (K) 0.5 mg/cm2
(Tested in accordance to IES-RP-CC-005.2)
4. Copper Strip Test: No Discoloration.
5. FTIR: Silicone oil, Amide, DOP not detectable. (Tested in accordance to IES-RP-CC-005.2)
6. Non-volatile residue: Max. 30 mg/g. (Tested in accordance to IES-RP-CC-005.2)
7. Surface Resistivity: Max. 10e11 ohms/square. (Tested in accordance to ASTM-D257)
8. Static Decay: Max. 3 seconds. (Tested in accordance to FTMS 101-C, 4046)
9. Triboelectric charge: Max. 50 volts.
10. Color: White.
11. Design and Feature: Ambidextrous, straight fingers, textured or smooth and beaded cuff.
12. Dimensions: Glove size Palm width (mm) Length (mm)
Extra-small 70 ±10 min. 240mm
Small 80 ±10 min. 240mm
Medium 95 ±10 min. 240mm
Large 110 ±10 min. 240mm
Extra-large 115 ±10 min. 240mm
13. Thickness: Location of thickness measurements
Finger (at 15mm from fingertip) min. 0.28mm
Palm (at center of palm) min. 0.20mm
14. Physical Properties: Before aging After aging
Tensile Strength (Mpa): Min. 18 (Before Aging) min. 16 (After Aging)
Ultimate Elongation (%): Min. 500 (Before Aging) min. 400 (After Aging)
15. Packaging: 100 pieces of gloves per double polybags, 10 polybags per master polybag, 1 master polybag per carton.
Note: Inner & outer polybags are manufactured & processed in Class 100 Cleanroom
16. Certificate of: A certificate of conformance is available upon request to ensure all products shipped conform to specified specification.
17. Quality Assurance: Manufactured under ISO 9002 Quality System.
Meet or exceed ASTM D3578-95 on water leak & dimension.
The information above is a guideline of typical performance values and characteristics of the products & not to be use as actual product specifications.