High Quality 8011 8006 Hydrophilic Aluminium Foil / Aluminum Fin for Air Conditioner
Aluminium fin foil :
hydrophilic aluminium foil finstock is widely used in household air conditioner ,refrigerrator ,cold equipment and vehicle air ec
1. alloy :1100,1200,1145,8011,8006
2. temper :h12,h14,h16,h18 ,h22,O
3. thicknes:0.08mm to 0.25mm
4. widht :20mm to 2100mm
our company ajust the alloy and develop DS-1,DS-2,DS-3 which are good in mechanical and hydrophilic capability on the basis of 1100,1200,1145,8006 with all kinds of size !
|
Place of Origin |
Zhejiang, China (Mainland) |
|
Brand Name |
Jinding |
|
Model Number |
1060 |
|
Grade |
1000 Series |
|
Thickness |
0.08mm --0.25mmm |
|
Width |
80mm --1240mm |
|
Application |
hydrophilic aluminium finstock |
|
Surface Treatment |
Coated |
|
Hardness |
30 |
|
Alloy Or Not |
Non-alloy |
|
Al (Min) |
99.5 |
|
Yield (≥ MPa) |
7o |
|
Temper |
O - H112 |
|
Ultimate Strength (≥ MPa) |
100 |
|
Elongation (≥ %) |
10 |
Product Brief Introduction:
() Aluminum Coil/Foil Used for Air Conditioner and Others (packing.Cable and pipe)
- Alloy ,temper,Physical Properties under Room Temperature
|
Alloy |
Temper |
Physical Properties under Room Temperature |
||
|
U.T.S 6 b ,Mpa |
Elongation e% |
Cupping Value IE,mm |
||
|
1100 1235 8079 |
O |
80110 |
≥20 |
≥6.0 |
|
H22 |
100135 |
≥16 |
≥5.5 |
|
|
H24 |
115145 |
≥12 |
≥5.0 |
|
|
H26 |
125160 |
≥8 |
≥4.0 |
|
|
H18 |
≥160 |
≥1 |
-- |
|
|
Mark: Special specifications you need can be negotiated and marked in the contract |
||||
|
Thickness & Tolerance mm |
Width & Tolerance mm |
Core I. D. mm |
Max. Roll O. D. mm |
Core Material |
|
0.0090.02 |
1001100 ±0.5 |
Φ75,Φ150,Φ200 |
Φ≤1400 |
Paper, Aluminum, Steel |
The Coat Properties of Hydrophilic Coated Foil:
|
No. |
Item Index |
Technology Index |
|
|
1 |
Film Thickness |
1.0-2.0μm(Average Thickness for Single Face) |
|
|
2 |
Hydrophilicity |
Initial Contact Angle |
Initial Contact Angle≤10° |
|
Persistent Contact Angle |
Persistent Contact Angle≤20° |
||
|
3 |
Adhesive Power |
Cupping Testing(5mm pressed by): no Flake |
|
|
4 |
Corrosion Resistance |
Salt Spray Testing(72 hours) |
|
|
5 |
Alkali Resistance |
Soaked in 20,20%NaOH for 3 minutes |
|
|
6 |
Solvent Resistance |
Weight Loss of Sample≤1% |
|
|
7 |
Stability |
under 200 for 5 min, the color will not change |
|
|
8 |
Oil Resistance |
Soaked in volatile oil for 24 hours without bubbling |
|
|
9 |
Coat Odor |
No Peculiar Odor |
|
|
10 |
Abrasion against Mould |
The Same as Common Aluminum Foil |
|