1. Chemical Composition of the Welding Wires(%)
C 0.06~0.15
Mn 1.40~1.85
Si 0.80~1.15
S ≤0.025
P ≤0.025
Cu ≤0.50
C 0.06~0.15
Mn 1.40~1.85
Si 0.80~1.15
S ≤0.025
P ≤0.025
Cu ≤0.50
2. Mechanical Properties of Welding Wires
σb ≥500MPa
σs ≥420MPa
δ5 ≥22%
Akv ≥27 (-30°C)
Mig Welding Wire is commonly use in high deposition rate welding process. The wire generates a stable arc and also have very low spatter during welding. It can weld using either CO2 Gas or Argon shielding Gas.
Luguang Wedling Wire can also weld in a consistent and continiuous manner (Long Weld) without any interruptions. Large gaps can be filled or bridged easily at all positions and is also easy to handle and does not require skill welder for easy operation. You only require to have minimal post weld cleaning and there is no stub loss as compared to covered electrodes.
All in all, the whole process is easy to operate, in addition, a better and clean environment. Below shows the area which CO2 Wedling Wire are widely used:
a) Automobile Industry
b) Motor Cycle & Bicycle
c) Ship Construction
d) Containers
e) Steel Furniture Industry
f) Steel Fabrication & Engineering
g) Gas Tanks & Fire Extinguishers
h) Other welding process