Key Specification/Special Features:
Applications:
Widely applied to marine industry
Protecting electrical splices, joint and terminations, electrical insulation where flame-retardant, water proof, UV resistance requires
Characteristics:
Flame retardant, polyolefin material with hot-melt adhesive
Meet: CE, RoHS
Operating temperature range:
Shrink temperature: 120 Degrees Celsius
Operating temperature:-55 Degree Celsius to 110 Degree Celsius
Specification:
Normal size (mm)
| As supplied (mm)
| After recovered (mm) | *Style
| Standard length (mm) | |
Inside diameter (min.) | Inside diameter (Max.) | Wall thickness (Min)
| |||
22/6 | 22 | 6 | 2.5 | O | 1000-1500 |
33/8 | 33 | 8 | 2.5 | O | 1000-1500 |
40/12 | 40 | 12 | 2.5 | O | 1000-1500 |
55/16 | 55 | 16 | 2.7 | O | 1000-1500 |
65/19 | 65 | 19 | 2.8 | O | 1000-1500 |
75/22 | 75 | 22 | 3.0 | O | 1000-1500 |
95/25 | 95 | 25 | 3.0 | O | 1000-1500 |
115/34 | 115 | 34 | 3.0 | O | 1000-1500 |
140/42 | 140 | 42 | 3.0 | O | 1000-1500 |
160/50 | 160 | 50 | 3.0 | O | 1000-1500 |
180/58 | 180 | 58 | 3.0 | O | 1000-1500 |
200/65 | 200 | 65 | 3.0 | O | 1000-1500 |
235/65 | 235 | 65 | 3.0 | O | 1000-1500 |
265/75 | 265 | 75 | 3.0 | O | 1000-1500 |
300/85 | 300 | 85 | 3.0 | O | 1000-1500 |
Technical Data:
Property | Test Method | Typical Data |
Tensile strength | ASTM D 2671 | ≥14MPa |
Tensile strength after aging | ASTM D 2671/158℃, 168hrs. | ≥12MPa |
Longitudinal change after shrinking | ASTM D 2671 | 0, -10% |
Elongation at break | ASTM D 2671 | ≥300% |
Elongation at break after aging | ASTM D 2671/120℃,168hrs. | ≥200% |
Dielectric strength | IEC 243 | ≥20KV/mm |
Heat shock (4hrs. at 225℃) | ASTM D 2671 | No cracking or flowing |
Volume resistance | IEC 93 | ≥1014ΩNaN |
Flammability | SAE-AMS-DTL-23053/5 | Self extinguish in 30 sec. |
Thermoplastic adhesive | ||
Water absorption | ISO 62 | <0.2% |
Softening point | ASTM D E28 | 85℃ |
Peel strength (PE) | DIN 30672 | 4 N/cm |
Copper stability | ASTM D 2671 | Non-corrosive |
Resistance to fungus and decay | ISO 846 | Pass |