Name:HBE-317L Stainless Steel Flux-cored Wire
Standard:GB/T17853 E317LT-1 AWS A5.22 E317LT-1 JIS Z3223 TS317L-FBI
Features:HBE-317L consists of low C-18Cr-12Ni-3Mo . It has excellent mechanical properties and suitable for all-position welding performance. Stable electric arc ,less spatter and better slug detachability when welding . It has excellent resistance to the pitting corrosion and intergranular corrsion by virtue of higher percentage of molybdenum .
Applications:Suitable for welding Cr19-Ni13-Mo3(317L) and Cr18-Ni12-Mo2-N(316LN) stainless steel . It is primarily applied to the welding of Petroleum refining ,chemical industry and surfacing repair .
Note: 1.Ensure the purity of shielding gas and mixing ratio of properly mixed gas is well controlled ,with flow at 20-25L/min.
2. Keep the electrode extension between 15-25mm.
3. Recommended current (DCEP)Wire to be in contacted with positive pole.
4. Please clean the appearance of base metal before welding .
5. Use the wire under the best possible condition . It should be used up as soon as possible if it's unpacked .
Typical all weld metal composition, (%)
TradeName | Item | C | Mn | Si | Ni | Mo | Cr | S | P |
HBE-317L | Standard | ≤0.04 | 0.5~2.5 | ≤1.0 | 12.0~14.0 | 3.0~4.0 | 18.0~21.0 | ≤0.03 | ≤0.04 |
Test | 0.025 | 1.21 | 0.50 | 12.40 | 3.50 | 19.16 | 0.005 | 0.020 |
Typical Properties of Deposited Metal
Trade Name | Test items | δb(MPa) | δ5(%) | Akv(0℃)(J) |
HBE-317L | Standard | ≥520 | ≥20 | ---- |
Test | 590 | 35 | ---- |
Welding Parameter Suggestions
Wire Diameter (mm) | Flat and Horizontal position | Vertical position | Overhead position | |||
A | V | A | V | A | V | |
1.2 | 140-220 | 23-33 | 120-180 | 24-28 | 160-200 | 26-30 |
1.6 | 200-300 | 27-32 | _ | _ | _ | _ |
We can develop different kind of quality products basing on customer's chemical composition and mechanical properties.
Please contact us with your requriement and we shall get back to you within 24 hours with confirmed feedback.