block Neodymium Iron Boron magnets have a very high energy product and coercivity, can pick up 660 times of own weight of heavy objects.
The advantage is high cost-effective, with good mechanical properties, easy cutting; according customer's demand to manufacture in a wide range of shapes, sizes and grades.
The shortcoming is easy to rust, oxidation, so the Sintered NdFeB's surface is usually required for plating such as zinc, nickel, copper,silver, gold, etc., can also be done phosphorus treatment or spray epoxy resin to slow down the oxidation rate.
Pic shows the magnet with NiCuNi coating and the grade is UH,it means max working temperature is 180 degree.
Grade | Residual Induction | Coercive Force | Intrinsic Coercive Force | Maximum Energy Product | Maximum Operating Temperature | ||||
Br | Hcb | Hcj | (BH)max | Tw | |||||
T | KGS | KA/m | KOe | KA/m | KOe | KJ/m3 | MGOe | ℃ | |
N28UH | 1.04-1.08 | 10.4-10.8 | 780-812 | 9.8-10.2 | ≥1990 | ≥25 | 207-223 | 26-28 | ≤180 |
N30UH | 1.08-1.12 | 10.8-11.2 | 804-844 | 10.1-10.6 | ≥1990 | ≥25 | 223-239 | 28-30 | ≤180 |
N33UH | 1.14-1.17 | 11.4-11.7 | 820-876 | 10.3-11.0 | ≥1990 | ≥25 | 247-263 | 31-33 | ≤180 |
N35UH | 1.17-1.21 | 11.7-12.1 | 860-907 | 10.8-11.4 | ≥1990 | ≥25 | 263-279 | 33-35 | ≤180 |
N38UH | 1.22-1.26 | 12.2-12.6 | 860-907 | 10.8-11.4 | ≥1990 | ≥25 | 287-303 | 36-38 | ≤180 |
N40UH | 1.26-1.29 | 12.6-12.9 | 860-907 | 10.8-11.4 | ≥1990 | ≥25 | 289-303 | 38-40 | ≤180 |
Note: The above mentioned data of magnetic parameters and physical are given at 20℃±2℃
block Neodymium Iron Boron magnets
block Neodymium Iron Boron magnets
The main physical properties of sintered NdFeB
magnetic properties | Parameters |
Density /g.cm3 Vickers Hardness HV Resistivity /υΩ.cm Compressive strength/N.mm-2 Coefficient of Thermal Expansion (C⊥)/K-1 Coefficient of Thermal Expansion (C∥) /K-1 | 7.45 570 150 780 4.8X10-6 -3.4X10-6 |