| Name | Film facd plywood |
| Film color | black / brown/ red |
Core Materials | poplar / hardwood |
Glue | phenolic resin / melamine/ urea-formaldehyde resin |
Size (mm) | 1220*2440 / 915*1830 |
| Usage | construction |
Reuse times | 10 - 15 |
| Packing | Inner packing: Inside pallet is wrapped with a 0.20mm plastic bag. Outer packing: Pallets are covered with plywood and then steel tapes for strength. |
| Surface abrasion | 0.04 g/100r |
| Bonding strength | 1.72 Mpa/mm2 |
| Modulus of elastictity | 5017 Mpa/mm2 |
| Crack, delaminating | NONE |
| Edge defects | NONE |
| Warpage degree | < 10% |
Market | Asia, Middle East, Africa, Europe, Latin America, Ect. |
Payment terms | L/C, TT, D/P |
Certificate | CE, ISO9001 |
advantages :
1.If put in boiling water for 48 hours, it is still glue-sticking and non-deformed
2.Physical mood is better than iron moulds and can satisfy the requirements of constructing mould, while the iron ones are easy to be deformed and can hardly recover its smoothness even after repairing
3. If used abide by the illustrations strictly, it can be reused more than 20 times, thus reducing the cost greatly and avoiding the disadvantages from ( rustily and erosive of iron mould)
4. Solves the problems of leaking and rough surface during constructing process
5.Particularly suitable for watering concrete project because it can make the concrete surface smooth and flat
6. Realizing a higher economic profits
Mechanics performance
| moisture content | <= 10% | |
| density | 0.75/Above cm3 | |
| wear value | <= 0.1g/100r (peaceful rice dregs) | |
| impact intensity | 40kj/M2 | |
| elasticity coefficient | >= 5000MPa >= 7948MPa; | |
| static tune intensity | >= 24MPa >= 75.8MPa | |
| angularity | <= 1% | |
| thickness expansion rate | (72 hours normal temperature water immersion) <= 8% |