1) Steel Grade:
1.2316,3Cr2Mo/P20/1.2312,1.2378
2) Dimensions: 10mm-800mm
3)Shape:Round Bars
3)Shape:Round Bars
4)Delivery condition:
EAF+LF+VD+(ESR), rolled / forged, annealed / Q+T, black/peeled/turned, UT tested
5)Delivery condition:30days after receive the payment in advance
EAF+LF+VD+(ESR), rolled / forged, annealed / Q+T, black/peeled/turned, UT tested
5)Delivery condition:30days after receive the payment in advance
6)Payment term: prepay 30% by T/T, the balance against L/C at sight or T/T
Chemical Composition(%) | |||||||
C | Si | Mn | P | S | Cr | ---- | ------ |
1.90-2.20 | 0.10-0.40 | 0.15-0.45 | ≤0.030 | ≤0.030 | 11.0-12.0 | --- | ------ |
Specialty | |||||||
High charcoal and chromium tool steel, have high penetration, small distortion, high rigidity, good endurance. | |||||||
Use | |||||||
1.Cold pressing mold extrusion with low pressing and burden, imprint mold, cold cutting scissor | |||||||
Heat Treatment | |||||||
1.Quench: 950-980`C cold oil(need re-preheat~500`C-850`C)HRC≥60 | |||||||
2.Eliminate stress, stabilize framework tempering, (180-200`C)≥2 hours HRC60-62 | |||||||
3.If it is necessary, it could be changed into 320-350`C≥2 hours backfire HRC≥60-62 | |||||||
4.Annealing: 780-800`C slow cooling | |||||||
Melting Process | |||||||
1. EAF: Electric Furnace+LF+VD(Optional) | |||||||
2. ESR:Electric Furnace+LF+VD+Eleroslag Remelted(Optional) | |||||||
UT Class | |||||||
According to Standard of SEP 1921/84,100% Volume, Level C/c, D/d or E/e | |||||||
Tolerance on Quantity | |||||||
+/-10% Per Size |
Packaging Details: Packed with steel wires,suitable for transporation
Delivery Detail: 30 days