Technical conditions for plates of SA387Gr22CL1 HIC
1. Scope
The technical conditions apply to plates of SA387Gr22CL1 HIC with thickness range 8mm-60mm.
2. Adopt standard:
ASME SA387/SA387M Specification for pressure vessel plates, alloy steel, Chromium-Molybdenum
ASME SA20/SA20M Standard Specification for General Requirements for Steel Plates for Pressure Vessels
ASME SA370 Standard Test Methods and Definitions for Mechanical Testing of Steel Products
3. Dimension, Shape, Weight and Permissible Deviation
The dimension, shape, weight and permissible deviation shall meet the requirements of ASME SA20/SA20M.
The thickness toleration: -0/+2.5mm
4. Technical conditions
4.1 Chemical composition (Ladle analysis)
The chemical composition of plates shall be accordance with the following table 1.
Table 1 Chemical composition (Ladle analysis)
Grade | Thickness mm | C | Si | Mn | P | S | Mo |
SA387Gr22CL1 HIC | Ladle analysis | 0.05- 0.15 | Max 0.50 | 0.30- 0.60 | Max 0.015 | Max 0.003 | 0.90- 1.10 |
Product analysis | 0.04- 0.15 | Max 0.50 | 0.26- 0.66 | Max 0.015 | Max 0.003 | 0.85- 1.15 |
Grade | Thickness mm | Cr | Ni | Cu | V | Nb | Ti | Als |
SA387Gr22CL1 HIC | Ladle analysis | 2.00- 2.50 | Max 0.40 | Max 0.40 | Max 0.03 | Max 0.020 | Max 0.03 | Min 0.015 |
Product analysis | 1.88- 2.62 | Max 0.43 | Max 0.43 | Max 0.03 | Max 0.030 | Max 0.04 | Min 0.015 |
4.2 Steel making process: EAF+LF/VD
4.3 Mechanical properties
The mechanical properties of SA387Gr22CL1 HIC shall meet the requirement as table 2&3.
Table 2 Tensile properties
Thickness mm | Yield strength MPa | Tensile strength MPa | Elongation % | Section shrinkage % |
8-110 | Min 205 | 415-585 | Min 18 | Min 40 |
4.4 Impact properties
Impact test in the longitudinal and transverse for plates of SA387Gr22CL1 HIC shall meet the requirements per table 3.
Table 3 Impact properties
Grade | Sampling size | Room temp. Transverse Akv(J) |
SA387Gr22CL1 | 10x10x55 | Min 27 |
7.5x10x55 | Min 21 | |
5x10x55 | Min 14 |
4.5 Hardness: Max 22HRC
4.6 SWHT: Simulated Post-Weld Heat Treatment of Mechanical Test Coupons shall be prepared in 600+/-10 C with min.5 minute per each mm of thickness.
4.7 NACE MR0175/ISO 15156-2 / Annex B.5 / Test method NACE TM0284 in solution-A sour service (CLR =< 5% & CTR =<5% & CSR =< 2% shall be reported)
4.8 Surface quality
The surface quality of plates shall be accordance with ASTM A20/A20M.
4.9 Ultrasonic inspection
Plates shall be ultrasonic inspected per ASTM A578/A578M level B.
4.10 Test method and inspection rules
Test items, sampling quantity, sampling method and test method shall conform to table 4.
Table 4 Test items for plates
Test item | Quantity, Piece | Sampling method | Test method | Sampling conditions |
Ladle analysis | 1 (per furnace) | ASTM A20/A20M | ASME SA370 | / |
Tensile test | 1 (per rolled pc) | ASTM A20/A20M | ASME SA370 | SWHT |
Charpy-V impact test at -20C | 3 (per rolled pc) | ASTM A20/A20M | ASME SA370 | |
Hardness | 1 (per rolled pc) | GB/T2975 | GB/T 230.1 | |
Product analysis | 1 (per rolled pc) | ASTM A20/A20M | ASME SA370 | +N |
Ultrasonic test | Each product pc | ASTM A578/A578M | ||
HIC test | See 5.HIC | NACE TM0284 | NACE TM0284 | SWHT |
5. HIC sampling method: Per heat number/ thickness/ heat treatment rules combine one group.
6. Package, marking and certificate
Package, marking and certificate shall conform to A20.
7. The third party inspection
The chemical composition, tensile test and Charpy -V impact test and HIC test for plates of SA387Gr22CL1 HIC shall be witnessed by surveyor of SGS.
8. Delivery conditions
The delivery conditions for plates of SA387Gr22CL1 HIC shall be Normalized+ Tempered.
9. Other requirements
The other requirements for plates of SA387Gr22CL1 HIC shall be accordance with SA387/SA387M-2010.
MTC accordance with EN10204: 2004 3.1