Descaled 420J2 ASTM INOX Hot Rolled Stainless Steel Coil 0.3mm - 15mm Thickness

Grade 

Description and General Uses

304

The most widely used stainless steel with the best all round performance. Its carbon

content is lower and its corrosion after welding resistance is higher than T302. It is less

susceptible to intergranular corrosion after welding. Non magnetic but slightly magnetic

when cold worked.

304L

A low carbon stainless steel with general corrosion resistance like T304, but with

superior resistance to intergranular corrosion following welding or stress relieving.

Highly recommended for parts which are fabricated by welding and which can not be

annealed. Generally limited to temperatures up to 426°C. The physical properties and

thermal treatments of T304L are similar but not identical to T304. Non magnetic when

annealed but slightly magnetic when cold worked.

316

Also known as Marine grade stainless steel. T316 has 2-3% Molybdenum which improves

corrosion resistance. T316 has superior corrosion resistance to other austenitic steels

when exposed to many types of chemical corrodents as well as marine environments

-T316 also has applications in the chemical, textile, and paper industries. It has better

strength and creep resistance at high temperatures than T304 and greater work

hardening properties. Non magnetic but slightly magnetic when cold worked.

316L

Has lower carbon than T316, with corrosion resistance similar to T316 but superior

resistance to intergranular corrosion following welding or stress relieving. It is

recommended for parts which cannot be subsequently annealed. Service temperaturesup to 

426°C. 

The physical properties and thermal treatments of type 316L are similar butnot identical to 

type 316. 

Non-magnetic when annealed but slightly magnetic when

cold worked.

310s

310S has been developed for high temperature service where high creep strength is

required. Max service temp is around 1100°C but it is not recommended for applications

of prolonged service as it may become brittle. Non magnetic when annealed or cold

worked.