Hastelloy C276 / UNS N10276 / 2.4819 Nickel Alloy Seamless Pipe ASTM B622
1. Grade: Incoloy 825
2. Process: VIR - VAR - ESR - Forging - Cold Rolling / Cold Drawing - Semifinished - Finished
3. Delivery Condition: Solution Annealed
4. Surface Condition: AP, BA, Polished
5. OD: 6-325mm
6. WT: 0.5-25mm
7. Length: Max. 25 meters
8. Specification: ASTM, ASME, GB, JIS, GOST, DIN, etc.
9. Packing: Plywood case, Bundle
Hastelloy C-276 Characteristics
Hastelloy C276 Alloy is a Ni-Cr-Mo alloy containing W and extremely low carbon and Si contents.
- Excellent resistance to a wide range of corrosive media, under oxidizing and reducing conditions
- Excellent resistance to pitting, crevice corrosion, and stress corrosion cracking.
Alloy C-276 Corrosion resistance
Hastelloy C276 Alloy can be used in many chemical processes with oxidizing and with reducing media. The high molybdenum and chromium contents render the alloy resistant to chloride ion attack. The tungsten content further increases this resistance. Hastelloy C276 Alloy is one of the few materials that is resistant to moist chlorine gas, hypochlorite and chlorine dioxide solutions. The alloy exhibits excellent resistance to concentrated solutions of oxidizing salts (such as iron (III) chloride and copper chloride).
Applications
Hastelloy C276 Alloy finds wide application in the chemical and petrochemical industry, for components in organic processes containing chlorides, and for catalytic systems. This material is especially suitable for use in situations where hot, contaminated mineral acids, solutions and organic acids (such as formic and acetic acid) as well as sea water are encountered.
- Pulp and paper industry, e.g. for digestion and bleaching vessels
- Scrubbers and special reheaters as well as wet-operating fans for combustion and flue gas desulphurisation systems
- Equipment and components for sour-gas service
- Reactors for acetic acid production
- Sulphuric acid coolers
- Methylene diphenyl isocyanate (MDI)
- Manufacture and processing of technically impure phosphoric acid
- Combustion-resistant alloy for high pressure oxygen applications
Chemical composition
|
|
Ni |
Cr |
Fe |
C |
Mn |
Si |
Mo |
W |
Co |
V |
P |
S |
|
min(%) |
bal. |
14.5 |
4.0 |
|
|
|
15.0 |
3.0 |
|
|
|
|
|
max(%) |
16.5 |
7.0 |
0.01 |
1.0 |
0.08 |
17.0 |
4.5 |
2.5 |
0.35 |
0.04 |
0.03 |