Iron-cobalt-vanadium soft magnetic alloy 1J22 permendur hiperco 50
Cross Reference
Country | Grades |
Russia(ГOCT) | 49KΦ2 |
USA(ASTM) | Hiperco 50a /permendur /Supermendur |
Japan(JIS) | SEM SMEV |
UK(BS) | Permendur |
France(NF) | AFK502 |
China(GB) | 1J22 |
Chemical Composition(%)
C | Mn | Si | P | S | Cu | Ni | Co | V | Fe |
≤0.04 | ≤0.30 | ≤0.30 | ≤0.02 | ≤0.02 | ≤0.2 | ≤0.5 | 49.0-51.0 | 0.8-1.8 | Remainder |
Physical Properties
Resistivity | 0.40 | μΩ.m | |
Density | 8.20 | g/cm3 | |
Curie Point | 980 | ºC | |
Tensile Strength | Non-annealed | 1325 | N/mm2 |
Annealed | 490 | N/mm2 | |
Curie Temperature | °F 1710 | °C 932 | |
Saturation induction at | H=250 oersteds(Kilogausses) 23 | H= 19.9 at/m(Telsa) 2.3 | |
Saturation magnetostriction | Change in unit length x 10-6 | 60 |
Magnetic Property
Type | Magnetic Induction at Different Magnetic Field Strength | Coercivity/Hc/(A/m)≤ | |||||
B400 | B500 | B1600 | B2400 | B4000 | B8000 | ||
Cold Rolled Strip | 1.6 | 1.8 | 2.0 | 2.1 | 2.15 | 2.2 | 128 |
Wire.Forgings | 2.05 | 2.15 | 2.2 | 144 |
Coefficient of Linear Expansion
Temperature | Coefficient | ||
68°F To | 20°C To | 10(-6)/°F | 10(-6)/°C |
392 | 200 | 5.28 | 9.5 |
752 | 400 | 5.61 | 10.1 |
1112 | 600 | 5.83 | 10.5 |
1472 | 800 | 6.28 | 11.3 |
Typical Mechanical Properties
Temperature | Hardness Rockwell B | |
°F | °F | |
1558 | 843 | 94 |
1598 | 870 | 89 |
1625 | 885 | 97 |
1692 | 925 | 92(Poor magnetic Properties) |
Heat Treatment
Heat Treatment
When selecting a heat treating temperature for the application, two factors should be considered:
• 1. For best magnetic soft characteristics, select the highest suggested temperature.
• 2. If the application requires specific mechanical properties higher than that produced when employing the highest temperature, select the temperature that will provide desired mechanical properties.
As temperature decreases, magnetic properties become less magnetic soft. Heat treating temperature for best soft magnetic properties should be 1625°F +/- 25°F (885°C +/- 15°C).Do not exceed 1652°F(900°C).
The heat treating atmosphere used must be nonoxiding and noncarburizing. Atmospheres such as dry hydrogen or high vacuum are suggested. Time at temperature should be two to four hours. Cool at a rate of nominally 180 to 360°F (100 to 200°C) per hour to a temperature of least 700°F(370°C), then cool naturally to room temperature
|
Heat Treatment Regime
Annealing | Quenching | Tempering | Normalizing |
√ | √ | √ | √ |
Range of Products
Product Type | Products | Dimension/mm | Processes | Deliver |
Plate/Sheet | Plate/Sheet | 1.0-40.0 | Hot Rolling and Cold Rolling | Cold State Soft State |
Rod |
Round Bar | 8.0-32.0 | Hot Rolled,burnished | Black, bright |
32.0-180 | Forging,Peeled, turned | Black, bright | ||
Coil/Strip | Coil/Strip | 0.05-1.5 | Cold Rolled,bright | Cold State Soft State |
Chemical composition,Physical and Mechanical properties will be engineered according to specific customer requirements.Therefore chemical composition,physical and mechanical properties might be different to values listed in this document.