ZG-P-3450/ZG-I-7249,Low-Hardness Shoe Sole PU Resin Manufacturer,Low Density Shoe Sole PU Resin
Low-Hardness Shoe Sole PU Resin Manufacturer
Low Density Shoe Sole PU Resin
Medium-high density PU Resin for shoe sole with the upper
Characteristic: High resilience, low density.
Application: Applicable to the production of insole for sports shoes and leather shoes.
Name of products | Appearance | Viscosity(Pa·s/50℃) | Density(g/cm3/40℃) | Package(kg) |
ZG-P-3450 | White or pale yellow, liquid, no foreign material | 0.80-1.40 | 1.16-1.20 | 18 |
ZG-I-7249 | Transparent liquid, no foreign material | 0.10-0.30 | 1.18-1.20 | 20 |
Typical properties of China High Resilience Insole PU Resin
Reference shipments ratio: A/B=31/22 (barrel)
Catalysts and auxiliary agents:
ZG-P-3450/ZG-AC-2/water =18kg/220g/80g
Note: corresponding adjustment should be made to the addition of auxiliary agent at different areas, different environment and different production conditions.
Low Density Low Hardness Sole Pu Molding conditions & physical properties:
Reactivity | Technical index | Test item | Reference physical properties |
Reference ratioP+C/I | 100/54-56 | Molded density of sole(g/cm3) | 0.32~0.34 |
Using temperature(℃) | material: 45-50; B material:38-42 | Hardness (type A) | 20~30 |
Cream time(s) | 9~13 | Tensile strength(MPa) | 4.5~5.5 |
Rise time(s) | 30~45 | Elongation(％) | 250~300 |
Metal mold temperature(℃) | 55~65 | NBS abrasion resistance(％) | ≥10% |
Demould time(min) | 7.0~10.0 | Free foam density(g/cm3) | 0.15~0.17 |
mm)Folding endurance (room temperature)(40,000 gap length, mm) | ＜8 |
High Resilience Insole PU Resin
Matching ratio is based on the optimal matching value which will vary with the category and additive amount of paint additives added.
Free foam density will vary with the seasons (temperature, humidity).
Stripping time will be extended with the increase of the thickness of moldings.
Folding endurance conditions: bending angle is 90 degrees and the frequency is 80 times / min * 40 thousand times
Data listed above is just for reference. The specific data is subjected to the practical operation. If other physical properties are required, please contact us.