CYG-KYNAR(150℃/175℃) FLAME-RETARDANT PVDF
HEAT-SHRINKABLE TUBINGS
.jpg)
.jpg)
CYG-KYNAR (150℃) FLAME-RETARDANT PVDF HEAT-SHRINKABLE TUBINGS
CYG-KYNAR (150℃) is clear, thin wall, flexible, flam-retardant with excellent chemical resistance, it is especially suitable for applications abrasion resistance and cut-through resistance, or superior chemical and solvent properties performance, Provides electrical insulation and strain relief of multipoint connectors and solder joints. Ideal for applications that require dense packing of components or visual inspection of covered components.
Equal Raychem:RN-150 & Sumitomo:K2/K3
Equal Raychem:RN-150 & Sumitomo:K2/K3
CYG-KYNAR (175℃) FLAME-RETARDANT PVDF HEAT-SHRINKABLE TUBINGS
CYG-KYNAR (150℃) is clear, thin wall, semi-rigid, flam-retardant with high temperature and excellent chemical resistance.Especially suitable for applications requiring high temperature performance, outstanding abrasion resistance and cut-through resistance, or superior chemical and solvent properties. Provides electrical insulation and strain relief of multipoint connectors and solder joints. They are for applications that require dense packing of components or visual inspection of covered components.
Equal Raychem:RW-175/KYNAR & Sumitomo: K
Standard:UL,224, SAE-AMS-DTL23053
Standard:UL,224, SAE-AMS-DTL23053
Specifications
Item | Test method | CYG-KYNAR(150℃) | CYG-KYNAR(175℃) |
Min. Shrink temperature | 140℃ | 155℃ | |
Operating temperature range | ASTM D792 | -55℃~+150℃ | -55℃~+175℃ |
Specific gravity | ASTM D2671 | 1.78g/cm3 | 1.78g/cm3 |
Tensile strength | ASTM D2671 | =>30MPa | =>34.5MPa |
Elongation at break | 225℃,168hrs | =>150% | =>150% |
Elongation at break after aging | 275℃,4hrs | =>100% | =>50% |
Heat shock | -55℃,4hrs | No cracking | No cracking |
Cold bend | ASTM D2671 | No cracking | No cracking |
Dielectric strength | ASTM D257 | =>15.7kv/mm | =>30kv/mm |
Volume resistivity | UL-224 | =>1013 OM.cm | =>1013 OM.cm |
Flammability | VW-1Pass | VW-1Pass |
Size
Size | Min. inside diameter as supplied(mm) | Max. inside diameter after recovery( mm) | Recovered wall Thickness(mm) |
3/64 | 1.2 | 0.6 | 0.25±0.05 |
1/16 | 1.6 | 0.8 | 0.25±0.05 |
3/32 | 2.4 | 1.2 | 0.25±0.05 |
1/8 | 3.2 | 1.6 | 0.25±0.05 |
3/16 | 4.8 | 2.4 | 0.25±0.05 |
1/4 | 6.4 | 3.2 | 0.33±0.05 |
3/8 | 9.5 | 4.8 | 0.33±0.05 |
1/2 | 12.7 | 6.4 | 0.33±0.05 |
4/3 | 19.1 | 9.5 | 0.43±0.08 |
1 | 25.4 | 12.7 | 0.48±0.08 |
1 1/2 | 38.1 | 19.1 | 0.48±0.08 |