Neodymium Iron Boron is a type of rare-earth permanent magnet. It is made from an alloy of neodymium, iron, and boron to form the Nd2Fe14B tetragonal crystalline structure. This material is currently the strongest type of permanent magnet in the world.
There are two kinds of magnets: Sintered NdFeB magnet and bonded NdFeB magnet.
This NdFeB rectangular block magnet is sintered NdFeB magnet,the magnetized through the thickness.
Nd-Fe-B permanent magnet is manufactured in a wide range of shapes, sizes and grades according customer's demand.
NdFeB has a very high energy product and coercivity, can pick up 660 times of own weight of heavy objects.
The advantage is high cost-effective, with good mechanical properties, easy cutting; according customer's demand to manufacture in a wide range of shapes, sizes and grades.
The shortcoming is easy to rust, oxidation, so the Sintered NdFeB's surface is usually required for plating such as zinc, nickel, silver, gold, etc., can also be done phosphorus treatment or spray epoxy resin to slow down the oxidation rate.
The EH grade and its details properties, the Maximum Operating temperature is under 200 degree.
pls see follow table.
pls see follow table.
Sintered NdFeB rectangular block magnet magnetic energy parameters
Grade | Residual Induction | Coercive Force | Intrinsic Coercive Force | Maximum Energy Product | Maximum Operating Temperature | ||||
Br | Hcb | Hcj | (BH)max | Tw | |||||
T | KGS | KA/m | KOe | KA/m | KOe | KJ/m3 | MGOe | ℃ | |
N28EH | 1.04-1.08 | 10.4-10.8 | 780-812 | 9.8-10.2 | ≥2388 | ≥30 | 207-223 | 26-28 | ≤200 |
N30EH | 1.08-1.12 | 10.8-11.2 | 804-844 | 10.1-10.6 | ≥2388 | ≥30 | 223-239 | 28-30 | ≤200 |
N33EH | 1.14-1.17 | 11.4-11.7 | 820-876 | 10.3-11.0 | ≥2388 | ≥30 | 247-263 | 31-33 | ≤200 |
N35EH | 1.17-1.21 | 11.7-12.1 | 860-907 | 10.8-11.4 | ≥2388 | ≥30 | 263-279 | 33-35 | ≤200 |
N38EH | 1.22-1.26 | 12.2-12.6 | 860-907 | 10.8-11.4 | ≥2388 | ≥30 | 287-303 | 36-38 | ≤200 |
Note: The above mentioned data of magnetic parameters and physical are given at 20℃±2℃
The above demagnazation durve is for 33EH magnet grade at difference temperature.
This magnet is coated white zinc,it has better resistant to corrosion. pls see the compare of salt spray test results for coating
APPLICATION:
The above demagnazation durve is for 33EH magnet grade at difference temperature.
The main physical properties of sintered NdFeB rectangular block magnet:
magnetic properties | Parameters |
Density /g.cm3 Vickers Hardness HV Resistivity /υΩ.cm Compressive strength/N.mm-2 Coefficient of Thermal Expansion (C⊥)/K-1 Coefficient of Thermal Expansion (C∥) /K-1 | 7.45 570 150 780 -4.8X10-6 -3.4X10-6 |
This magnet is coated white zinc,it has better resistant to corrosion. pls see the compare of salt spray test results for coating
Commonly type of coating | Coating thickness(um) | Neutral salt spray test | ||||
dark Ni | Cu | Shine Ni | Total | |||
Single-layer Ni | 25 | 25 | 24h | normal | ||
Double-layer Ni | 12 | 10 | 25 | 72h | better | |
Dark Ni-Cu–shine Ni | 6.25 | 8.75 | 10 | 25 | 120h | excellent |
APPLICATION:
magnetic magnetization device
micro motors,
electronic industry,
sound device magnetic suspension system,
magnetic transmission machine
magneto therapy equipment
MRI
magnetic machine
magnetic equipment
magnetic water
magnetic seal
oil magnetization of paraffin
magnetic connection,
magnetic drive,
Permanent magnet crane
electromagnetic pumps
magnetic thrust axis,
magnetic machinery,
magnetic spring,
magnetic vibration device
magnetic separators