din 1.3355 high speed steel bars equivalents:
T1/W18Cr4V/1.3355 steel
high speed steel bars T1 high speed tool steel round bar heat treatment :annealed
1.1.3355 high speed steel bar process:EAF+LF+VD, hot rolled / hot forged
2.1.3355 hss steel bar Certificate: ISO9001 and MTC report provided.
3.Delivery time: 10-20 days
4.The minimum order quantity is 3 ton.
2.1.3355 hss steel bar Certificate: ISO9001 and MTC report provided.
3.Delivery time: 10-20 days
4.The minimum order quantity is 3 ton.
hss steel bars forged:
The forging temperature for high speed steels is 1050°/1150°C. Do not charge direct into the high temperature part of the furnace, but pre-heat slowly to 850°/900. The heat should then be increased more quickly to the forging temperature. If, during the forging, the temperature of the material drops below 880/900°C, re heating will be necessary. Cool very slowly after forging.
hss steel bars 1.3355 high speed tool steel bar annealed:
The forging temperature for high speed steels is 1050°/1150°C. Do not charge direct into the high temperature part of the furnace, but pre-heat slowly to 850°/900. The heat should then be increased more quickly to the forging temperature. If, during the forging, the temperature of the material drops below 880/900°C, re heating will be necessary. Cool very slowly after forging.
hss steel bars 1.3355 high speed tool steel bar annealed:
The Most Benefits Yo Can Get From Shouze :
• Competitive prices
• Saving time
• Free solution advice from experienced engineers
• Free solution advice from experienced engineers
• One -stop ware house saving your money and labour
• Lowst overseas transport cost and speedy delivery
T1/W18Cr4V/1.3355 high speed steel hss steel bar chemical composition (%) :
Standard | Steel Grade | C | Si | Mn | P | S | Cr | Mo | V | W | other |
DIN | 1.3355 | 0.70-0.78 | ≤0.45 | ≤0.40 | 0.030 | 0.030 | 3.80-4.50 | 1.00-1.20 | 17.50-18.50 | ||
ASTM | T1 | 0.65-0.80 | 0.20-0.40 | 0.10-0.40 | 0.030 | 0.030 | 3.75-4.50 | 0.90-1.30 | 17.25-18.25 | ||
GB | W18Cr4V | 0.70-0.80 | 0.20-0.40 | 0.10-0.40 | 0.030 | 0.030 | 3.80-4.40 | <0.30 | 1.00-1.40 | 17.50-19.00 |
2 1.3355 high spedd steel specification/.Size:
round | diameter(mm) | length(mm) | |
50~510 | 2000~6000 | ||
plate/sheet | thichkness(mm) | width(mm) | length(mm) |
35~500 | 50~1200 | 2000~6000 |
3 1.3355 high speed steel.hardness of annealed:
HBS≤240-300 |
4.1.3355 high speed steel process
EAF+LF+VD+ESR+Forged Heat Treatment(optional) |
5.1.3355 high speed steel condition of surface
black | rough machined(peeled) | turned |
hss steel bars 1.3355 high speed tool steel round bar sizes availability:
Flats • Hollowbar • Metric • Non-Standard • Rounds • Squares • Standard
hss steel bars applications:
| Blanking Dies | Boring Tools | Broaches |
| Center Drills | Gear Cutters | Lamination Dies |
| Lathe Tools | Mandrels | Milling Cutters |
| Planer Tools | Punches | Reamers |
| Router Bits | Shear Blades | Taps |
| Thread Chasers | Twist Drills | Wood Knives |
hss steel bars forged:
The forging temperature for high speed steels is 1050°/1150°C. Do not charge direct into the high temperature part of the furnace, but pre-heat slowly to 850°/900. The heat should then be increased more quickly to the forging temperature. If, during the forging, the temperature of the material drops below 880/900°C, re heating will be necessary. Cool very slowly after forging.
The forging temperature for high speed steels is 1050°/1150°C. Do not charge direct into the high temperature part of the furnace, but pre-heat slowly to 850°/900. The heat should then be increased more quickly to the forging temperature. If, during the forging, the temperature of the material drops below 880/900°C, re heating will be necessary. Cool very slowly after forging.