High Quality LLDPE Recycled Granules
- Fiber (Carpet, Textiles, Upholstery, etc.)
- Film (Shopping bags, casting film, multilayer film, etc.)
- Blow Molding (Medical & Cosmetic container, Lubricant & Paint container, etc)
- Extrusion Molding (Sheet, Pipe, Wire & Cable, etc.)
- Injection Molding (Automotive, Electronic, Construction, House wares, Furniture, Toys, etc.)
1, LLDPE film grade
Tests | Value | Unit |
Melt Flow Rate (MFR) | 2.0±0.4 | g/10min |
Density | 920±2 | Kg/cm3 |
Tensile Strengthat Yield | 8 | Mpa ≥ |
Tensile Strengthat Break | 12 | Mpa ≥ |
haze | 15 | %≤ |
Packing | In 25 kg PP woven bags,20MT/20'FCL | |
2, LLDPE for Master Batch Use
Tests | Value | Unit |
Melt Flow Rate (MFR) | 20 | g/10min |
Density | 0.924 | g/cm3 |
Tensile Strength | MD12 | Mpa |
TD 10 | ||
Elongation at Yield | 13 | % |
Elongation at Break | 200 | |
Dark Drop Impact | 105 | g |
Brittle Temperature(F 50) | -70 | °C |
Vicat Softening Point | 90 | °C |
Packing | In 25 kg PP woven bags,20MT/20'FCL | |
3, LLDPE Powder Rotational Molding Grade for Tank Use
Tests | Value | Unit |
Melt Flow Rate (MFR) | 3.2 | g/10min |
Density | 0.939 | g/cm3 |
Melting Point | 127 | °C |
Tensile Yield Strength | 21 | Mpa |
Tensile Strength at Break | 28 | Mpa |
Elongation at Break | 1,100 | % |
Flexural Modulus | 750 | Mpa |
Brittle Temperature | <-60 | °C |